Oxidized (Blown) Bitumen
Oxidized (Blown) Bitumen
We are also capable of producing other grades of Blown Bitumen upon request by our customers.
Technical Advantages
Durability
Flexibility
Water Resistant
Chemical Stability
Application
Blown grade bitumen shall be broken up into small pieces and heated slowly to the application temperature of 220ºC to 230ºC.
Packing
20 & 50 Kg Kraft Paper Bags with Inner Lining , 200 Kg Steel Drums
Specification
Characteristic R 10/20 R 85/25 R85/40 R115/15 Method
Relative density 1.00 - 1.06 1.00 - 1.06 1.00 - 1.05 1.01 - 1.06 ASTM D70
at 25 º C, g/ml
Softening point 90 min 80-90 80-90 100-120 ASTM D36
(Ring and Ball), º C
Penetration 10-20 20-30 35-45 1-20 ASTMD5
at 25 º C , 0.1 mm
Flash point 200 200 200 200 ASTMD92
(Cleveland Open Cup) º C
Loss on heating 0.5 0.2 0.5 0.2 ASTMD6
% by mass
Ductility 2 3 3 2 ASTMD113
at 25 º C cm, min
Solubility 99 99 99 99 EN 12592 : 2000
in toluene % wt min